XFEM-based Numerical Analysis of Residual Stresses and Defect Nocivity in FSWeld AA6082-T6 Aluminum Alloy

Document Type : Research Paper

Authors
Houda Salmi 1
Houda Lifi 1
Mohamed Ouakarrouch 1
Amal Lamarti 2
Abdelilah Hachim 2
1 Cadi Ayyad University, UCA, Marrakesh, ENSA, MISCOM Laboratory, Safi, Morocco
2 Dept. Hassan II University of Casablanca (UH2C), ENSEM, Laboratory of Mechanics, Engineering and Innovation, ISEM, Casablanca, Morocco
10.22055/jacm.2025.48565.5328
Abstract
This work introduces a sequential framework integrating explicit thermomechanical finite element analysis with the eXtended Finite Element Method (XFEM) to evaluate the severity of residual stresses and defects in friction stir welded (FSW) AA6082-T6 aluminum joints. The thermal evolution and residual stress distributions are first computed in Abaqus/Explicit using a moving heat source model, validated against thermocouple measurements from the literature, with an average temperature deviation below 3%. A mesh convergence study confirms the reliability of the solution, showing less than 3% variation in the stress intensity factor (KI) between consecutive refinements. Subsequently, XFEM coupled with the Level Set method is employed to simulate crack growth under thermo-mechanical loading, following the maximum energy release rate (MER) criterion. Findings indicate that a rotational speed of 800 rpm lowers peak temperatures by 10% and longitudinal residual stresses (S11) by 30% relative to 1100 rpm. At elevated temperatures (~700 K), a significant increase in KI is observed due to pronounced thermal softening and degradation of material properties, highlighting the critical role of thermal effects on crack driving forces. This integrated approach enables a mesh-independent and accurate assessment of defect severity, providing a reliable tool for optimizing FSW parameters to enhance the structural integrity of aerospace-grade aluminum joints.
Keywords
Friction Stir Welding
Residual Stresses
Crack Propagation
XFEM-Level Set Method
Thermomechanical simulation
Subjects

Publisher’s Note Shahid Chamran University of Ahvaz remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

[1] Verma, S., Kumar, V., Kumar, R., Sidhu, R.S., Exploring the application domain of friction stir welding in aluminum and other alloys, Materials Today: Proceedings, 50, 2022, 1032–1042.
[2] Nagaraja, S., Anand, P.B., Mariswamy, M., et al., Recent Advances in Friction Stir Welding of Dissimilar Al–Mg Alloys for Aerospace Applications: A Review, Reviews on Advanced Materials Science, 64(1), 2024, 20240033.
[3] Heidarzadeh, A., et al., Friction stir welding/processing of metals and alloys: A comprehensive review on microstructural evolution, Progress in Materials Science, 117, 2021, 100752.
[4] Li, D., Slater, C., Cai, H., Hou, X., Li, Y., Wang, Q., Joining technologies for aluminium castings—A review, Coatings, 13, 2023, 958.
[5] Meng, X., Huang, Y., Cao, J., Shen, J., dos Santos, J.F., Recent progress on control strategies for inherent issues in friction stir welding, Progress in Materials Science, 115, 2021, 100706.
[6] Guo, Y., Li, P., Effect of residual stress and microstructure on the fatigue crack growth behavior of aluminum friction stir welded joints, Materials, 17(2), 2024, 385.
[7] Salih, O.S., Ou, H., Sun, W., Heat generation, plastic deformation and residual stresses in friction stir welding of aluminium alloy, International Journal of Mechanical Sciences, 238, 2023, 107827.
[8] Ma, Z., Feng, A., Chen, D., Shen, J., Recent advances in friction stir welding/processing of aluminum alloys: Microstructural evolution and mechanical properties, Critical Reviews in Solid State and Materials Sciences, 43(4), 2018, 269–333.
[9] Gite, R.A., Loharkar, P.K., Shimpi, R., Friction stir welding parameters and application: A review, Materials Today: Proceedings, 19, 2019, 361–365.
[10] Mosayyebi, E., Albaghdadi, B.M., Ghiasvand, A., Guerrero, J.W.G., A-Derazkola, H., Investigation of the effect of loading angle on mixed-mode fatigue crack propagation of AA2024-T351 friction stir welded joint, International Journal on Interactive Design and Manufacturing, 18(4), 2024, 2545–2558.
[11] Ge, M., Liu, Y., Zhu, L., Zeng, G., Wang, Z., Chen, K., Tang, W., Mechanical properties and fracture mechanism of double-sided friction stir welded Al-Mg-Si alloy joints, Engineering Failure Analysis, 171, 2025, 109840.
[12] Dorbane, A., Harrou, F., Sun, Y., et al., Machine Learning for Modeling and Defect Detection of Friction Stir Welds: A Review, Journal of Failure Analysis and Prevention, 25, 2025, 110–139.
[13] Choudhary, A., Jain, P.K., Numerical simulation of material flow and defect formation during FSW to predict weld failure location, Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, 2024, DOI: 10.1177/09544054241229478.
[14] Seidi, S., Yaghoubi, S., Shirazi, A., Employment of fuzzy inference system in prediction of optimal solution area for thermal stress generated in the friction stir welding process, Expert Systems with Applications, 278, 2025, 127342.
[15] Beygi, R., et al., Mechanism of toughness enhancement of brittle fracture by intermittent η-intermetallic in Al/Cu joint made by FSW, Materials Science and Engineering: A, 890, 2024, 145907.
[16] Salmi, H., El Had, K., El Bhilat, H., Hachim, A., Numerical analysis of the effect of external circumferential elliptical cracks in transition thickness zone of pressurized pipes using XFEM, Journal of Applied and Computational Mechanics, 5(5), 2019, 861–874.
[17] Salmi, H., Hachim, A., El Bhilat, H., El Had, K., Numerical modeling and comparison study of elliptical cracks effect on the pipes straight and with thickness transition exposed to internal pressure, using XFEM in elastic behavior, Journal of Computational & Applied Research in Mechanical Engineering, 10(1), 2020, 229–244.
[18] Salmi, H., El Had, K., El Bhilat, H., Hachim, A., Numerical study of SIF for a crack in P265GH steel by XFEM, in: Recent Advances in Mathematics and Technology: Proceedings of the First International Conference on Technology, Engineering, and Mathematics, Kenitra, Morocco, March 26–27, 2020, 105–127.
[19] Elmeguenni, I., Mazari, M., Numerical investigation on stress intensity factor and J-integral in friction stir welded joint through XFEM method, Fracture and Structural Integrity, 13(47), 2019, 54–64.
[20] Elmeguenni, I., Asymptotic response of friction stir welded joint under cyclic loading, Frattura ed Integrità Strutturale, 15(58), 2021, 202–210.
[21] Abotaleb, M., Modélisation numérique du procédé de soudage par friction-malaxage: application aux alliages d'aluminium, Ph.D. Thesis, Université de Lille, 2023.
[22] Al-Badour, F., Merah, N., Shuaib, A., Bazoune, A., Coupled Eulerian Lagrangian finite element modeling of friction stir welding processes, Journal of Materials Processing Technology, 213, 2013, 1433–1439.
[23] Toric, N., Brnic, J., Boko, I., Brcic, M., Burgess, I.W., Uzelac, I., Experimental analysis of the behaviour of aluminium alloy EN 6082AW T6 at high temperature, Metals, 7, 2017, 126.
[24] Payandeh, M., Sjölander, E., Jarfors, A.E., Wessen, M., Mechanical and thermal properties of rheocast telecom component using low silicon aluminium alloy in as-cast and heat-treated conditions, Light Metals 2015, Springer, 2015, 209–214.
[25] Wilson, A., The thermal expansion of aluminium from 0 to 650 °C, Proceedings of the Physical Society, 53, 1941, 235.
[26] Jaspers, S., Dautzenberg, J., Material behaviour in conditions similar to metal cutting: Flow stress in the primary shear zone, Journal of Materials Processing Technology, 122(2–3), 2002, 322–330.
[27] SteelPro Group, H13 Tool Steel – Technical Data, Technical Report, 2023, Available at: https://steelprogroup.com/tool-steel/grades/h13/properties/technical-data/
[28] Nandan, R., DebRoy, T., Bhadeshia, H., Recent advances in friction-stir welding–process, weldment structure and properties, Progress in Materials Science, 53, 2008, 980–1023.
[29] Kumar, K., Kalyan, C., Kailas, S.V., Srivatsan, T.S., An investigation of friction during friction stir welding of metallic materials, Materials and Manufacturing Processes, 24(4), 2009, 438–445.
[30] Zhang, S., et al., Numerical analysis and analytical modeling of the spatial distribution of heat flux during friction stir welding, Journal of Manufacturing Processes, 33, 2018, 245–255.
Journal of Applied and Computational Mechanics
Volume 12, Issue 2
Spring 2026
Pages 569-593